Chemistry Nitronic 50 Chemical Requirements Ni Cr Mo Mn C Si Fe Max 13.5 23.5 3.00 6.0 0.06 1.00 Bal Min 11.5 20.5 1.50 4.0 Nitronic 50 Tensile Data Mechanical Property Requirements Ultimate Tensile Yield Strengtd (0.2% OS) Elong. R/A Hardness Min 100 KSi 55 KSi 35% 55% Max 293 Min 690 MPa 380 MPa Max There are other high strength properties available for sizes of bar, wire, sheet and plate. Inquire with a sales associate at High Perf...
Product Detail
FAQ
Product Tags
Chemistry
Nitronic 50 Chemical Requirements |
|||||||
|---|---|---|---|---|---|---|---|
| Ni | Cr | Mo | Mn | C | Si | Fe | |
| Max | 13.5 | 23.5 | 3.00 | 6.0 | 0.06 | 1.00 | Bal |
| Min | 11.5 | 20.5 | 1.50 | 4.0 | |||
Nitronic 50 Tensile Data
Mechanical Property Requirements |
|||||
|---|---|---|---|---|---|
| Ultimate Tensile | Yield Strengtd (0.2% OS) | Elong. | R/A | Hardness | |
| Min | 100 KSi | 55 KSi | 35% | 55% | |
| Max | 293 | ||||
| Min | 690 MPa | 380 MPa | |||
| Max | |||||
There are other high strength properties available for sizes of bar, wire, sheet and plate. Inquire with a sales associate at High Performance Alloys for more information. See bulletin, or brochure on the material (above) for a quick overview.
Specifications |
|
|---|---|
| Form | Standard |
| Metal Type | UNSS20910 |
| Bar | ASTM A193 ASTM A194 ASTM A276 ASTM A479 AMS 5764 |
| Wire | |
| Sheet | ASTM A240 AMS 5861 |
| Plate | ASTM A240 AMS 5861 |
| Fitting | |
| Forging | ASTM A182 ASTM A193 ASTM A 194 ASTM A276 ASTM A479 AMS 5764 |
| Weld Wire | A5.9 ER209 |
| Din | 1.4565 |
Annealing Temperature
NITRONIC 50 Stainless Steel can be supplied annealed at 1950 F to 2050 F (1066 C to 1121 C). For most applications, the 1950 F (1066 C) condition should be selected, as it provides a higher level of mechanical properties along with excellent corrosion resistance. When as-welded material is to be used in strongly corrosive media, the 2050 F (1121 C) condition should be specified in order to minimize the possibility of intergranular attack.
Corrosion Properties
Armco NITRONIC 50 Stainless Steel provides outstanding corrosion resistance – superior to Types 316, 316L, 317 and 317L in many media. For many applications the 1950 F (1066 C) annealed condition provides adequate corrosion resistance and a higher strength level. In very corrosive media or where material is to be used in the as-welded condition, the 2050 F (1121 C) annealed condition should be specified. High-Strength (HS) NITRONIC 50 bars are useful for applications such as shafting and bolting, but do not quite exhibit the corrosion resistance of the annealed conditions in all environments.