Inconel 600 UNS Trademark JIS W.Nr N06600 Inconel600 NCF600 2.4816 Inconel 600 Chemical composition: Alloy % Ni Cr Fe C Mn Si Cu P S 600 Min. 72 14 6 Max. 17 10 0.15 1 0.5 0.5 0.015 0.015 Inconel 600 Physical properties: Density 8.4 g/cm3 Smelt 1370-1425 ℃ Inconel 600 Alloy minimum Mechanical properties in the room temperature: Aolly status Tensile strengthRm N/mm2 Yield strengthRP0.2 N/mm2 ElongationA5 % Brinell hardnessHB Annealing treatment 550 240...
Detalle del producto
Preguntas más frecuentes
Etiquetas de productos
Inconel 600
UNS | Marca | JIS | W.Nr |
N06600 | Inconel600 | NCF600 | 2.4816 |
composición Inconel 600 química:
Aleación | % | Ni | cr | Fe | do | Minnesota | Si | Cu | PAG | S |
600 | Min. | 72 | 14 | 6 | ||||||
Max. | 17 | 10 | 0,15 | 1 | 0.5 | 0.5 | 0,015 | 0,015 |
Inconel 600 Propiedades físicas: Densidad
8,4 g / cm3
Eperlano
1370-1425 ℃
Inconel 600 propiedades de la aleación mínimo mecánicos en la temperatura ambiente:
estado Aolly | Resistencia a la tracción Rm N / mm2 |
resistencia a la fluencia Rp0,2 N / mm2 |
AlargamientoA5% | Dureza Brinell media pensión |
tratamiento de recocido | 550 | 240 | 30 | ≤195 |
tratamiento de solución | 500 | 180 | 35 | ≤185 |
Inconel 600 Característica de la siguiente manera : 1. Buena propiedad de resistencia a la corrosión para la reducción, oxidación, nítrico y otros medios. 2.Bien la corrosión bajo tensión propiedad de resistencia tanto en la temperatura ambiente y alta temperatura. Resistencia a la corrosión 3.Good del cloro y cloro hidruro seco. Propiedad 4.Bueno mecánica cuando por debajo de cero, la temperatura ambiente y alta temperatura. 5.good anti-fluencia resistencia a la rotura, con la recomendación de 700 ℃ o por encima de ambiente de trabajo. Inconel 600 Metallurgical structure
600 is face-centered cubic lattice structure. Inconel 600 Corrosion resistance
600 have corrosion resistance to many kinds of corrosive media. The material produced by Beall Industry group are of high quality.Chromium content made it with better corrosion resistance than Nickel 99.2 (alloy200) and Nickel 99.2 ( alloy201,low carbon) in the oxidize environment. Meantime, high Nickel content make this alloy with good corrosion resistance in the reduction condition and alkaline solution, and also effective avoid chlorine-iron stress corrosion cracking. 600 have good corrosion resistance in the acid, acetic acid, formic acid, stearic acid and other organic acid, with medium corrosion resistance in the inorganic acid. The alloy with excellent corrosion resistance in the first and the second recycling use of the high purity water in the nuclear reactor. Especially excellent corrosion resistance to dry chlorine and chlorine hydride applied up to 650 ℃. When nder the high temperature, annealing and state solution alloy have good antioxidant off and high-intensity in the air, 600 can resist the ammonia, nitriding and carburizing atmosphere, but at the turn of the changes in redox conditions, it will be corrosion by parts of oxidation media.( such as green death liquid)
Inconel 600 Application field :
1. Erosion thermocouple sheath of the atmosphere
2.Vinyl chloride monomer production: corrosion resistance to chlorine, hydrogen chloride, oxidation and carbonation.3. Oxide shaft chloride converted to six fluoride: hydrogen fluoride anti-corrosion.4. Corrosive alkali metal produce and usage filed, especially the sulfide use environment.5. Use Chlorine produce titanium dioxide
6.Organic or inorganic chlorine produce: corrosion resistance to chlorine and fluoride.
7. Nuclear reactor
8.Heat treatment furnace flask and components, especially in the carbonization and nitride atmosphere.9. Petrochemical works production of catalytic regeneration in the application of more than 700℃ recommended the use of 600, in order to obtain a longer service life