N08811 / Incoloy 800HT
Introduction Super alloys are also referred to as high performance alloys. They have good creep and oxidation resistance, and are utilized where high surface stability is required. They also have an ability to function under high temperatures and mechanical stress. They can be strengthened by solid-solution hardening, work hardening, and precipitation hardening. They are divided into three groups such as iron-based, nickel-based, and cobalt-based alloys. Incoloy 800HT™ is a nickel-iron-chromi...
Super alloys are also referred to as high performance alloys. They have good creep and oxidation resistance, and are utilized where high surface stability is required. They also have an ability to function under high temperatures and mechanical stress. They can be strengthened by solid-solution hardening, work hardening, and precipitation hardening. They are divided into three groups such as iron-based, nickel-based, and cobalt-based alloys.
Incoloy 800HT™ is a nickel-iron-chromium alloy, and also a modified version of alloy 800. It has high creep-rupture strength. The following datasheet gives an overview of Incoloy 800HT™.
The chemical composition of Incoloy 800HT™ is outlined in the following table.
|Iron, Fe||≥ 39.5|
|Nickel, Ni||30- 35|
|Manganese, Mn||≤ 1.50|
|Silicon, Si||≤ 1|
|Copper, Cu||≤ 0.75|
|Sulfur, S||≤ 0.015|
The physical properties of Incoloy 800HT™ is displayed in the following table.
|Density||7.94 g/cm³||0.287 lb/in³|
|Melting point||1357-1385 °C||2475-2525 °F|
The following table shows the mechanical properties of Incoloy 800HT™.
|Tensile strength (annealed)||560 MPa||81200 psi|
|Yield strength (annealed)||250 MPa||36300 psi|
|Elongation at break (annealed prior to test)||45%||45%|
The thermal properties of Incoloy 800HT™ are given in the following table.
|Thermal expansion co-efficient (@ 20-100°C/68-212°F)||14.4 µm/m°C||8.00 µin/in°F|
|Thermal conductivity||11.5 W/mK||79.8 BTU in/hr. ft².°F|
Other designations that are equivalent to Incoloy 800HT™ include:
Fabrication and Heat Treatment
Incoloy 800HT™ can be machined using conventional machining methods which are used for iron based alloys. Machining operations are performed using machining coolants. High-speed operations such as grinding, turning, or milling, are performed using water-base coolants. Drilling, broaching, tapping, or boring can be performed using heavy lubricants.
Incoloy 800HT™ can be formed using all conventional techniques.
Incoloy 800HT™ is welded using shielded metal-arc welding, gas-tungsten arc welding, gas metal-arc welding, and submerged-arc welding methods.
Incoloy 800HT™ can be heat treated by annealing. However, it does not harden by heat treatment.
Incoloy 800HT™ is forged at 1010 to 1205°C (1850 to 2200°F).
Incoloy 800HT™ is hot worked at 872 to 1205°C (1600 to 2200°F).
Incoloy 800HT™ can be cold worked using standard tooling.
Incoloy 800HT™ is annealed at 1149°C (2100°F) followed by cooling.
Incoloy 800HT™ is hardened by cold working only.
Incoloy 800HT™ is used in petrochemical equipments for heat exchangers.
|Thickness：0.40-4.75mm，General Width：1000、1219、1500mm||Whole Coil or piece of it||Cold Annealed，Surface 2B、2E|
|Thickness：4.76-60mm，Width：1500、2000、2500mm，Length：3000、6000、8000、8500mm（Under 10mm plate can be coiled）||Whole Coil or piece of it||Single hot rolling，Solid solution annealed state，Surface 1D|
|Thickness：0.10-3.0mm，Width：50-500mm||Whole Coil or Specified size||Cold Annealed，Surface 2B、2E|
Bar & Rod
|Rolled barΦ5-45mm，Length≤1500mm||Polished Bar（circle、Square）||Solution annealing,descaling|
|Outer diameterΦ4.76-135mm，Wall Thickness0.25-4.00mm，Length：≤35000 mm||Base on your requirement||Use for PHE|
|Outer diameterΦ3-114mm，Wall Thickness0.2-4.5mm||Base on your requirement||Use for PHE|
|Outer diameterΦ0.1-13mm||Base on your requirement||Ni & Ni alloy, Ti & Ti alloy|
|roundness and square alloy||Base on your requirement||Steel, Alloy|
|All kinds of Flangs||Base on your requirement||Steel, Alloy|
|Coil wire Φ0.90mm/1.2mm/1.6mm||Base on your requirement||Certificate of Origin：America, Sweden, Britain, Germany, Austria, Italy, France.|
|Elbow, three links, four links, different diameter size||Base on your requirement||Ni & Ni alloy, Ti & Ti alloy|
Explosive bonded laminate
|Raw Sheet Thickness≥2mm||Base on your requirement||Ni & Ni alloy, Ti & Ti alloy|